| Fase Nd2Fe14B1 | |||
| Estr. Crist. | Tetragonal | ||
| Grupo de espacio (nš) | P42/mnm (136) | ||
| Parametros de red (Ams) | a=8.80 c=12.20 | ||
| Temperatura de Curie (K) | 585 | ||
| at. | X | Y | Z |
| Nd | 0.266 | 0.266 | 0.0 |
| Nd | 0.139 | -0.139 | 0.0 |
| Fe | 0.224 | 0.568 | 0.128 |
| Fe | 0.039 | 0.359 | 0.176 |
| Fe | 0.097 | 0.097 | 0.205 |
| Fe | 0.318 | 0.318 | 0.247 |
| Fe | 0.5 | 0.5 | 0.113 |
| Fe | 0.0 | 0.5 | 0.0 |
| B | 0.368 | -0.368 | 0.0 |
| Fase alpha-Fe | |||
| Estr. Crist. | bcc, tipo W | ||
| Grupo de espacio (nš) | I m -3 m (229) | ||
| Parametros de red (Ams) | a=2.8665 | ||
| Temperatura de Curie (K) | 1015 | ||
| at. | X | Y | Z |
| Fe | 0.0 | 0.0 | 0.0 |
| Fase Fe2B | |||
| Estr. Crist. | Tetragonal, tipo Al2Cu | ||
| Grupo de espacio (nš) | I 4 / m c m (140) | ||
| Parametros de red (Ams) | a=5.110 c=4.249 | ||
| Temperatura de Curie (K) | 1030 | ||
| at. | X | Y | Z |
| Fe | 0.1649 | 0.6649 | 0.0 |
| B | 0.0 | 0.0 | 0.25 |
| Fase Fe3B | |||
| Estr. Crist. | Tetragonal, tipo Ni3P | ||
| Grupo de espacio (nš) | I -4 (82) | ||
| Parametros de red (Ams) | a=8.665 c=4.297 | ||
| Temperatura de Curie (K) | 780 | ||
| at. | X | Y | Z |
| Fe | 0.0775 | 0.1117 | 0.2391 |
| Fe | 0.3649 | 0.0321 | 0.9765 |
| Fe | 0.1689 | 0.2200 | 0.7524 |
| B | 0.2862 | 0.0487 | 0.4807 |